HydraTite™ Internal Pipe Joint Seal

HYDRATECH 8001 WATERLINE EPOXY

HYDRATECH 8001 WATERLINE EPOXY FAST FACTS

A High Build, solvent free epoxy lining system.
Approved for potable water contact in the United States (ANSI/NSF 61).
Low temperature cure down to 37ºF (3ºC).
Fast recommissioning time at minimum cure temperature of 37ºF (3ºC).
Fully trained application specialists.
Compatible with a variety of substrates.
Full contract support services, when required.
A high build, solvent-free, epoxy lining system for potable water applications
The HydraTech Waterline product is a fast-curing, solvent-free epoxy coating.
To date, potable water contact approval has been granted by:
NSF International (ANSI/NSF 61) United States for pipe ≥ 4 inches in diameter and tanks ≥ 5 gallons

A low temperature cured lining system for equipment, vessels and pipes which require approval for contact with drinking water for human consumption.

Surfaces must be sound and free from grease, dust and, if possible, all moisture.

Color	Base - Black Hardener - White Mixed - Gray
Mix Ratio (by volume)	2:1 V/V Base: Hardenr
Working Life –68ºF (20ºC)	15 minutes
Dry Times – 40ºF (3ºC)	Touch - 3 hours Hard - 6 hours Useable - 16 hours
Wet FIlm Thickness (mils)	40 (1000μ)
Dry FIlm Thickness (mils)	40 (1000μ)
% Vol Solids	100
Theoretical Coverage Rate (m/l)	1
Flash Point	Above 212ºF (100ºC)
Storage Life	Twelve months when stored in origianl sealed containers, between 50-77ºF (10-25ºC)
Tensile Strength (MPa)	22.26
Elongation at Yield (%)	1.18
Young's Modulus (MPa)	1814
Compressive Yield Strenth (MPa)	118.67
Flexural Strength (MPa)	38.21
Coating to Concrete Bond Strength (N)	3316
Coating to Metal Bond Strength (N)	2808

Minimum Application Temperature	40ºF (3ºC)
Manimum Relative Humidity	85%
Substrate Temperature	5ºF (3ºC) above dew point
Thinning	Not Recommended
Brush/Roller Application	Multi-coats are necessary to achieve correct film thickness. To aid application at low temperatures, both components should be warmed to 60-68ºF (15-20ºC) prior to mixing. Mix and apply as quickly as possible.
Airless Spray Application	See Airless Details
Cleaning Fluid	Universal Equipment Cleaner

Appearance	Base - Black Thixotropic Liquid Reactor - White Liquid
Odor	Base - Very Mild Reactor - Strong Amine Odor
Composition	Base – Epoxy Resin, Iron Oxide, Thixatrope Reactor – Aliphatic Amine, Silica, Titanium Dioxide
% Volitiles	Base - 0% Reactor - 0%
Flash Pint (Abel Closed Cup)	Base – 212ºF (100ºC) Reactor -212ºF (100ºC)
O.E.L. (8 Hours)	Base – Unknown Reactor – Unknown
LD50 (Indications Only)	Base – Unknown Reactor – Unknown

Inhalation	Wear suitable respiratory cartridge mask in enclosed spaces. Work in well ventilated areas.
Eyes	Wear suitable goggles
Skin	Wear protective clothing and gloves made of impervious material
Storage	Store away from direct sunlight and sources of heat. Do not allow temperature to exceed 77ºF (25ºC)

Inhalation	Effect – Headache, dizziness. Emergency First Aid – Remove into fresh air; loosen collar; do not walk around.
Swallowing	Effect – Irritation. Emergency First Aid – Do not induce vomiting; seek medical advice.
Eyes	Effect – Irritation. Emergency First Aid – Flush with clean water for ten minutes; seek medical advice.
Skin	Effect – Irritation. Emergency First Aid – Remove contaminated clothing, wash thoroughly with soap and water

Clean-Up Method	Scrape up excess material or absorb onto sand or sawdust and place in sealable containers. Ventilate area, avoid inhalation of vapors.
Waste Disposal	See MSDS

Extinguising Methods	Fire Carbon Dioxide, Dry Powder, Water Mist
Special Procedures	Do not inhale vapors.
Unusual Hazards	Dangerous to aquatic life. Do not let uncured material enter the water course.

Equipment	Dual component feed hot airless spray
Spray Temperature	95º-115º (35-45ºC)
Spray Pressure	Minimum 2200 psi at the tip
Nozzle Size	19-21 thou tip 60º nozzle angle
Working Time (@104ºC)	Maximum 5 minutes